Our company adopts the polyester dipped cord fabric produced by imported advanced equipment at home and abroad. It has the advantages of high modulus, fatigue resistance, and low dry heat shrinkage. It is an ideal framework material for high-performance semi-steel radial tires. The products have common types. There is also a high modulus and low yield type.

The main specifications are: 1670dtex, 1440dtex, 1100dtex and many other varieties, and can be customized according to customer specific requirements.

Physical Properties of Dipped Conventional Polyester Tire Cord Fabric:

Item		Unit	Specifications
Item		Unit	1100dtex/2	1440dtex/2	1670dtex/2
Break strength		N per end	≥140.0	≥180.0	≥205.0
EASL (elongation at specific load)	44.1N	％	4.5±1.0
	58.0N	％		4.5±1.0
	66.6N	％			4.5±1.0
Elongation at break		％	15.0±2.0	15.0±2.0	15.0±2.0
Adhesion (H-Test)		N/10cm	≥125.0	≥130.0	≥140.0
Coefficient of variation of break strength		％	≤5.0	≤5.0	≤5.0
Coefficient of variation of elongation at break		％	≤6.5	≤6.5	≤6.5
Dip pick up		％	3.5±1.0	3.5±1.0	3.5±1.0
Cord gauge		mm	0.56±0.03	0.61±0.03	0.66±0.03
Twist number	Ply twist	T/m	450±15	400±15	370±15
Twist number	Cable twist	T/m	450±15	400±15	370±15
Thermal shrinkage		％	≤3.5	≤3.5	≤3.5
Unpacking moisture		％	＜1.0	＜1.0	＜1.0

Note:

1.For adhesion(H-Test) experiment, vulcanization condition: temperature(138±2)℃, time 50min，pressure 3 MPa.

2.For thermal shrinkage test: temperature (177±2)℃，time 2 min，load 0.05CN/dtex .

3.The above are the normal specifications and technical standards. If any special indices are requested in dimension stability, twist number, fabric width, warp and weft density, or roll length, etc., our company can tailor-make it for you.

[ BACK ]

Add: No.185, West Yunhe Road, Guangling District, Yangzhou, China

Tel: +86-514-87200419　Fax: +86-514-87204105　Mobile: +86-13815833420

E-mail: sales@yangtaichem.com

Product Search

Search keyword: Specialty Chemicals for Polyester | Phosphate series flame retardant and plasticizer | Specialty Fibre | Rubber/Tire Reinforcement Materials |